Thermal conductive powder TFP-150J
Thermal conductive composite powder can build a complete thermal conductivity pathway in the adhesive, endowing it with good heat dissipation characteristics, and can also serve terminals, providing new heat dissipation solutions on some electronic components and heating components
Product Features
Hue white
Good liquidity
Stable thermal storage
Excellent thermal conductivity
Product Parameters
| Model | Average Particle Size (um) | Oil Absorption Value (g/100g) | Appearance | 105 ℃ volatile matter% |
| TFP-100Y | 18.34 | 8.6 | White Powder | 0.33 |
| TFP-150Y | 9.29 | 10.2 | White Powder | 0.35 |
| TFP-200Y | 12.55 | 13.4 | 白色粉末 | 0.31 |
Application Data
Preparation of 1.0-2.3W/(m.K) silicone thermal conductive potting adhesive, unit mass fraction
| Experimental Group | Additive Amount | 150cs Vinyl Silicone Oil | Hydrogen Containing Silicone Oil | Inhibitor | Pt Catalyst |
| TFP-100Y | 280~330 | 100 | 18.5 | 0.03 | 0.3 |
| TFP-150Y | 450~580 | 100 | 18.5 | 0.03 | 0.3 |
| TFP-200Y | 650~750 | 100 | 18.5 | 0.03 | 0.3 |
Prepare potting adhesive based on the group allocation ratio in the table above, and heat and vulcanize it at 100 ° C for 5 minutes to obtain a sample (2mm). The relevant application data of the test sample are as follows
| Experimental Group | Apparent State | Mobility(15cm) | Viscosity(mPa.s) | Thermal ConductivityW/(m.K) | Flame Retardant Level | Density(g/cm3) | Hardness A |
| TFP-100Y | Milky White | 3s | 3403 | 1.10 | V-0 | 1.62 | 68 |
| TFP-150Y | Milky White | 7s | 6426 | 1.58 | V-0 | 1.71 | 69 |
| TFP-200Y | Milky White | 10s | 8655 | 2.03 | V-0 | 2.17 | 72 |
Application Area
Epoxy system
Polyurethane system
Organic silicon system
Notes
If the thermal conductivity and viscosity requirements need to be adjusted, the feedback data of the test sample should be communicated with our relevant personnel to ensure consistency in the testing method and application experimental conditions. Our thermal conductivity composite powder process and ratio should be adjusted according to your company's relevant needs;
If there are issues related to storage stability, such as bottom hardening after 30 days under 50 ° C thermal storage conditions, our company will perform composite treatment on the relevant samples and communicate with your company to balance the relationship between viscosity and storage stability.